Friction and wear behavior of WC-Ni coatings HVOF sprayed on duplex stainless steel
Gespeichert in:
Zeitschriftentitel: | IOP Conference Series: Materials Science and Engineering |
---|---|
Personen und Körperschaften: | , |
In: | IOP Conference Series: Materials Science and Engineering, 770, 2020, 1, S. 012075 |
Format: | E-Article |
Sprache: | Unbestimmt |
veröffentlicht: |
IOP Publishing
|
Zusammenfassung: | <jats:title>Abstract</jats:title> <jats:p>The friction and wear behavior of high-velocity oxygen-fuel (HVOF) sprayed WC-Ni coatings was investigated. WC-Co coating was used as reference sample. Pin-on-disc tests were conducted on WC-Ni and WC-Co coatings surface in both pure water and 3.5% (wt.) saline solution, respectively. It was found that WC-Co coatings has superior wear and corrosion resistance in pure water due to their high hardness. However, cracks were observed in the wear scar of WC-Co coating, which wear rate was 2-4 times higher than that of WC-Ni coatings. The corrosion-wear resistance is not only affected by coating hardness, but also by powder composition. So WC-CrNi coating displays an excellent wear-and corrosion-resistance performance in saline solution.</jats:p> |
---|---|
Umfang: | 012075 |
ISSN: |
1757-8981
1757-899X |
DOI: | 10.1088/1757-899x/770/1/012075 |